Non-Shrinkage grouting material

Non-Shrinkag grouting material self leveling non-shrinkage early strength: 30Mpa in 4hours high strength Polar Bear Non-Shrink grouting material is blended through a special procedure by specially selected cementitious material, carefully selected fine aggregate and admixture. It owns the characteristics of high flow, non-shrinkage, early strength and high strength. Functionally they are divided into two categories include four products: High strength, Extra early strength.Properties1.Double expansion in plastic and hardened state, compensate the dry shrinkage, ensure the fixed combination between steel-back plane and concrete base, efficiently transmit the load carrying into the base.2. High early strength: this material is obtained by special cement as its basic material, it is suitable for urgent repair and accelerators construction under negative temperature environment.3.High fluidity.4.Easily used, only mixed with water on site, easily pumped.5.Durability: High final strength, excellent impermeability and corrosion resistance, ensure accuracy of equipment setting.6.Working environment: this material can be operated in a negative temperature environment with a rapidly increased strength.7. Non-chloride: no harm for equipment or armature reinforcementUses:1. Heavy equipment, High precision grinder.2. Erection Engineering of Structural steel3. Grouting to column foundation, pile foundation and Rock foundation to fixation.4. Anchoring of frame structure joint5. Repair to the honey-comb and holes of reinforced concrete structure6. Repair & Reinforcement to concrete structure.

Technical Data

(test in standard lab)

Name		HS-1	HS-2	EES-1	EES -2
Grain size	4.75mm/%	2.0
Setting time(min)	Initial	≥120		≥45
Bleeding capacity/%		1.0
Fluidity /mm	Initial	≥260
	30min	≥230
Compressive (Mpa),≥	4h	-	-	30	-
	12h	-	-	-	10
	1d	35	22	50	45
	3d	55	40	55	55
	28d	80	70	70	70
Height change %	1d
Bond strength (MPa)	28d	≥4.0
Erosion to armature		none
W/C		0.15	0.16	0.12	0.15
Operating temperature		≥5		≥-5

Using methods:Foundation treatment:1. Scaling and cleaning will be applied to the concrete base2. Solvent should be adopted to clear up the rust and oil on the bottom (the surface that will contact grout) of equipment3. Molding board joint should be treated well to ensure grouting material wont leak.4. Before grouting ,keep the concrete bed wet without waterMixing1.Pour required amount water into the barrel first, then add a bag of material stir for about 5 minutes.2. When stirring, the stir vane should move up and down, left and right along the barrel side in order to make the materials adhered to the bottom and side involved in mixing operation. The stir vane is not allowed to be above the mixture to avoid the invasion of air.3. If grout thickness more than 100mm, 5-10mm clean crushed stone should be added.4. Ensure enough mixing ability for continuous operating.Grouting:1. Mixed grouting material should be used out before lost its fluidity2. Grouting should begin from one side intend to avoid release entrapped air3. Coordinating mixing ability with grouting speed well for continuous operating4. Grouting surface should be a little higher than designed peak. In case of not need this part, it can remove before hardeningCuring:Ahead of hardening, all the uncovered parts should be cured well according to the concrete curing demandShelf life:6 months for High strength and 3months for Extra early strengthPackage and estimationPackage Grouting material 5kg/bag Consumption Mixed paste bulk 12.5L/bag Weight per cubic meter 2200kg

Non-Shrinkage grouting material